Trifluorostyrene sulfonic acid membranes

Abstract

This disclosure is directed to fluorocarbon polymers, polymeric membranes, and electrochemical cells and processes. The polymers and membranes are produced by radiation techniques to provide improved products. For example, α,β,β-trifluorostyrene in an inert organic solvent is grafted onto an inert film, such as tetrafluoroethylene-hexafluoropropylene copolymer, by irradiation, i.e. with Co-60 gamma radiation at a dose of several Mrad. The grafted film is then sulfonated, preferably in a chlorosulfonic acid bath. The resulting film is useful as a membrane or diaphragm in various electrochemical cells such as chlor-alkali or fuel cells.

Claims

What is claimed is: 1. A membrane adapted for use in electrochemical cells comprising: a. an inert polymeric base film; and b. sulfonated α, β, β-trifluorostyrene irradiation grafted on said film. 2. A membrane according to claim 1 wherein said inert polymeric base film is selected from the group consisting of polypropylene film, polyethylene film, polytetrafluoroethylene film, polytrifluorochloroethylene film, tetrafluoroethylene-hexafluoropropylene copolymer film, tetrafluoroethylene-ethylene copolymer film and laminated films thereof. 3. A membrane according to claim 1, wherein the percentage graft is in the range of about 3 to about 50%. 4. A membrane according to claim 3, wherein the percentage sulfonation is in the range of about 5 to about 25%. 5. A process for the preparation of a membrane suitable for use in electrochemical cells comprising: a. forming a solution of α, β, β-trifluorostyrene in an inert organic solvent; b. placing said solution in contact with an inert polymeric film; c. irradiating said contacted film to graft polymerize said trifluorostyrene onto the film; d. removing excess solution from said film; and e. sulfonating said grafted film. 6. A process according to claim 5 wherein said irradiating is with gamma radiation at a total radiation dose of about 0.1 to about 10.0 Mrad. 7. A process according to claim 5, wherein the organic solvent is selected from the group consisting of aromatic compounds and halogenated compounds. 8. A process according to claim 5, wherein the organic solvent is selected from the group consisting of benzene and methylene chloride. 9. A process according to claim 5, wherein the irradiating is carried out at a temperature in the range of about -78° C to about 60° C. 10. A process according to claim 5, wherein the sulfonation step is carried out by: a. forming a solution of halosulfonic acid which has a concentration in the range of about 5 to about 50%; and b. immersing said grafted film in said solution. 11. A method for the grafting of a perfluorinated vinyl monomer onto an inert polymeric film comprising: a. placing the perfluorinated vinyl monomer in contact with the inert polymeric film, b. irradiating the contacted film with gamma radiation at a total radiation dose of about 0.1 to about 10.0 Mrad. 12. A membrane adapted for use in an electrochemical cell comprising: a. an inert polymeric film b. a perfluoro vinyl monomer irradiation-grafted on said film, and c. a pendant ion-exchange group on said vinyl monomer.
BACKGROUND Chlorine is produced almost entirely by electrolytic methods, primarily from aqueous solutions of alkali metal chlorides. In the electrolysis of brines, chlorine is produced at the anode, and hydrogen, together with an alkali metal hydroxide, such as sodium or potassium hydroxide, at the cathode. As the anode and cathode products must be kept separate, many cell designs have been developed. These designs have generally utilized either a diaphragm, or a mercury intermediate electrode to separate the anolyte and catholyte compartments. In the diaphragm process, brine is fed continuously into the electrolytic cell and flows from the anode compartment through an asbestos diaphragm into the catholyte compartment which contains, for example, an iron cathode. To minimize back-diffusion and migration, the flow rate is always such that only part of the salt is converted. The hydrogen ions are discharged from the solution at the cathode, forming hydrogen gas and leaving hydroxyl ions. This catholyte solution, which contains sodium hydroxide and unchanged sodium chloride, is evaporated to obtain the sodium hydroxide. In the course of the evaporation the sodium chloride precipitates, is separated, redissolved, and sent back into the electrolytic cell. The function of the diaphragm is to maintain the level of concentration of alkali, to minimize the diffusional migration of hydroxyl ions into the anolyte and to maintain separation of hydrogen and chlorine. The diaphragm should also have minimal electrical resistance. In the mercury electrode process, the cation, after discharge, forms an alloy or amalgam with mercury. The amalgam flows or is pumped to a separate chamber in which it is allowed to undergo galvanic reaction, most often with water, to form hydrogen and a comparatively strong sodium hydroxide solution containing almost no sodium chloride. The diaphragm process is inherently cheaper than the mercury process, but as the former process does not provide chloride-free alkali, additional processing steps are necessary to purify and concentrate the alkali. Substitution of an ion-exchange membrane material for the diaphragm has been proposed. Numerous membrane materials have been suggested. For example, membranes are described in U.S. Pat. Nos. 2,636,851; 2,967,807; 3,017,338; and British Patent Nos. 1,184,321 and 1,199,952. Such membranes are substantially impervious to hydraulic flow. During operation, brine is introduced into the anolyte compartment wherein chlorine is liberated. Then, in the case of a cation permselective membrane, sodium ions are transported across the membrane into the catholyte compartment. The concentration of the relatively pure caustic produced in the catholyte compartment is determined by the amount of water added to this compartment from an external source, and by migration of water, in the cell, i.e. osmosis and/or electro-osmosis. While operation of a membrane cell has many theoretical advantages, its commercial application to the production of chlorine and caustic has been hindered owing to the often erratic operating characteristics of the cells. A number of disadvantages have been present when using these membranes, including a relatively high electrical resistance, poor permselectivity and oxidative degeneration. In membrane-type fuel cells, a fuel, such as hydrogen or a material which decomposes to hydrogen, is oxidized in an oxidation zone or chamber giving up electrons to an anode. The hydrogen ions formed migrate by means of an ion-exchange resin to the reduction zone or chamber where they combine with oxygen gas from an oxidant reduced at the cathode. Water, which contains a minor amount of a peroxide by-product, is discharged from the cell. Thus, both material and electrical charge balances are maintained as electrons flow from the anode to the cathode. This electron flow can be utilized to provide useful electrical energy. Numerous types of membranes have been proposed for use in fuel cells including polymers of α, β, β-trifluorostyrene (U.S. Pat. No. 3,341,366) and copolymers of trifluorovinyl sulfonic acid (British Pat. No. 1,184,321). It is an object of this invention to provide an improved cation permselective membrane for use in chlor-alkali cells and fuel cells which has a low electrical resistance and a high resistance to hydroxyl migration. It is a further object to provide a membrane which is particularly resistant to oxidative degradation, particularly in chlorine and peroxide environments. It is a still further object to provide chlor-alkali cells of the diaphragm type with improved electrical properties and which prevent chloride contamination of the catholyte material. And it is an object to provide improved fuel cells of the ion-exchange membrane type. It is also an object of this invention to provide a novel method for the preparation of membranes and the use of such membranes in electrochemical cells. Further objects will become apparent to one skilled in the art from the following detailed specification and the appended claims. THE INVENTION This invention relates to novel polymeric membranes, the method of making the membranes, and their use in electrochemical cells such as a diaphragm type chlor-alkali cell and an ion-exchange type fuel cell. Radiation techniques are used for the polymerization of perfluoro-olefinic monomers, and for the grafting of such monomers onto base films for use in electrochemical cells. The electrochemical cells in which the membrane described herein is to be used, are similar to previously used cells, subject to the modifications described herein. Generally, an enclosure is provided which is defined into a catholyte and anolyte compartment by the membrane material. In a chlor-alkali diaphragm cell, the catholyte compartment contains an appropriate cathode, generally a metallic material, such as iron. The anolyte compartment contains a conductive electrolytically-active anode, such as graphite or more desirably, a metallic anode having a valve metal substrate, such as a titanium, bearing a coating which contains a precious metal, precious metal oxide or other electrocatalytically active corrosion-resistant material or mixtures thereof. The anolyte compartment is provided with an outlet for generated chlorine gas, an inlet for brine solution and an outlet for depleted brine. Similarly, the catholyte compartment will have outlets for liquid (caustic) and gaseous (hydrogen) products and generally, an inlet through which water and/or sodium hydroxide solution may be added initially. Multicompartment cells may also be used, which have one or more buffer compartments, porous sheets and cationic membranes. In operation, a direct current is passed between the electrodes causing the generation of chlorine at the anode and the selective transport of hydrated sodium ions across the membrane into the catholyte compartment wherein they combine with hydroxide ions formed at the cathode by the electrolysis of water. The improved membrane of this invention is manufactured by the process of radiation grafting a fluorinated vinyl compound, such as α, β, β-trifluorostyrene (TFS), onto an inert polymeric film, and then sulfonating the membrane. The preparation of membranes by radiation grafting techniques has the advantage of permitting the use of a wide variety of film bases which may be tailored for the desired end-use, and the flexibility of grafting to the base a predetermined quantity of functional groups. Moreover the membranes made by this technique do not require the use of fillers and plasticizers which are used when fabricating membranes from conventionally made polymers, such as poly α, β, β-trifluorostyrene. The membranes made by this invention are therefore homogeneous, integral films which are directly usable in electrochemical cells. The choice of base film material to which the fluorinated vinyl compounds of this invention can be grafted should be chosen from polymeric film materials which are resistant to oxidative degradation. For example, grafting can be carried out on films of polymers of ethylene, propylene, tetrafluoroethylene (TFE), trifluorochloroethylene, and other halogenated olefinically unsaturated monomers preferably having 2-3 carbon atoms and films of copolymers of these monomers such as copolymers of tetrafluoroethylene-hexafluoropropylene (FEP) and TFE-ethylene. It has been found that it is preferable to utilize fluorocarbon base films rather than hydrocarbon base films. Such films are somewhat more inert, particularly under long-term and extreme conditions. In many instances, the desired end use of the membrane will dictate the choice of base film. For example, when the membrane is to be used in a chlor-alkali cell, the fluorocarbon base films should be used, as the other films will be degraded by the chlorine which is produced during operation of the cell. At the present, FEP film is convenient for commercial use; it is readily available as a staple article in commerce in 48 inch width rolls, while TFE is not so available. A laminate of FEP films, TFE films, or a combination may be used. A three layer laminate having a layer of TFE cloth sandwiched between two layers of FEP is an example of a useful membrane material. It may also be desirable to utilize a supported film. For example, the film material may be supported and laminated to a polymeric cloth, woven mesh, perforated sheet or foraminous support member to provide greater mechanical strength. The following description of the invention will be illustrated using FEP film as the base material. The thickness of the base film for grafting purposes is not critical. However, generally a greater percentage of graft is obtained when using a thinner film under similar conditions. As with the choice of film material, the choice of film thickness will depend on the end use of the membrane. The electrical resistance of the finished membrane is generally lower when starting with a thinner film, due to the greater percentage of grafting when utilizing the thinner films. If similar graft percentages are obtained for thick and thin films, then the electrical resistances of each will be approximately equal. FEP films ranging in thickness from 1/2 to 20 mils, perferably about 2 mils to about 5 mils, provide satisfactory base films for use in chlor-alkali cells. There is substantially no hydroxyl migration from the catholyte to the anolyte compartments when using a 5 mil film. Generally, films having a thickness of up to 10 mils are useful in fuel cells where greater mechanical strength or resistance to back-pressure is required. The monomeric materials to be grafted onto the base film generally comprise one or more fluorinated vinyl compounds such as perfluoro alkenyl aromatic monomers. These monomers may be depicted by the general formula: ##STR1## wherein x is an integer from zero to eight and the expression (CF 2 )x includes linear and branched-chain perfluoroalkyl groups. These are compounds which have had all of the non-aromatic carbon-hydrogen bonds replaced by carbon-fluorine bonds. It has been found that under extreme oxidative conditions such as are found in chlor-alkali and fuel cells, primary degradation of the material occurs at the C-H bonds. Membranes made from these fluorinated compounds will have a much greater lifetime than those containing C-H bonds. As C-H bonds on an aromatic ring are resistant to oxidation, the presence of non-fluorinated aromatic moities in the monomer are not detrimental. The foregoing monomers, or mixtures thereof, may be directly grafted onto the base film and then sulfonated, or the monomers may first be sulfonated and then grafted onto the base film. The aromatic groups provide ready sites for sulfonation by procedures described below. Alternatively sulfonated fluoroalkenyl monomers may be used. These monomers are preferably prepared in the sulfonated form and then grafted onto the base film. For example, one or more monomers of the general formula. F(CF.sub.2).sub.x CF = CF SO.sub.2 F wherein (CF 2 ) x is as defined above, may be grafted onto a base film and then hydrolyzed to a suitable form (i.e., an acid, alkali metal salt, ammonium or amine form), see U.S. Pat. Nos. 3,041,317, 3,560,568 and 3,624,053. The foregoing perfluorinated monomers may also be co-grafted with other monomeric materials such as those monomers known to be susceptible to radiation grafting. For example, α, β, β-trifluorostyrene can be co-grafted with α-methylstyrene onto a base film and then sulfonated to form a useful membrane. A preferred starting material is α, β, β-trifluorostyrene (TFS). This material may be made in accordance with several well known methods, such as those described in U.S. Pat. Nos. 3,489,807, 3,449,449 and 2,651,627. This invention will be further illustrated utilizing this compound as the monomer. It should be noted that the pure TFS is not required for this process. As the grafting will generally be done from solution due to economic considerations, commercial TFS containing other materials may be used. It is necessary, however, that the diluent be inert and a non-solvent for the base film. This means that the diluent must not either homopolymerize, nor copolymerize with the TFS under the radiation conditions of this process, nor adversely affect the radiation grafting. The general procedure for the graft polymerization of TFS onto the base film, used in each of the following embodiments, is as follows. The film base, covered with an interlayer of paper and wound into a roll, is placed in a chamber. A solution of trifluorostyrene in a suitable solvent is then added to completely immerse the film base roll. A vacuum and nitrogen flush is applied and re-applied several times to remove any dissolved oxygen from the solution and chamber. The chamber, under a nitrogen atmosphere, is sealed. The temperature is kept sufficiently low during this procedure to prevent vaporization of the solvent. The film and trifluorostyrene solution, in the sealed chamber, are irradiated i.e. for about two weeks at a suitable dose rate, as discussed below. The grafted film is then removed from the chamber and washed and dried. The grafting may be performed either using TFS in bulk or in solution. Generally, the solvent must have similar properties as described for the TFS diluent discussed above. Table I illustrates the grafting of TFS onto FEP film at different concentrations of TFS. The percentage of graft is determined by the difference between the weight of the final grafted film less the weight of the original base film, divided by the weight of the original base film. TABLE I______________________________________GRAFTING OF TRIFLUOROSTYRENEAT DIFFERENT CONCENTRATIONS______________________________________TFS Conc. Benzene Dose Rate Total Dose Graft______________________________________10% 90% 7236 r/hr 2.59 Mrad 1.4%30% 70% 7236 r/hr 2.59 Mrad 8.2%50% 50% 7236 r/hr 2.59 Mrad 14.3%70% 30% 7236 r/hr 2.59 Mrad 24.0%______________________________________ As can be seen from Table I the amount of graft increases with the concentration of TFS. The amount of graft for membranes useful in chlor-alkali cells may vary widely, such as from 3 to 40%, and preferably from about 10 to 30% of TFS graft. Hence, the TFS concentration in the grafting procedure should be varied accordingly. Membranes designed for use in fuel cells should have a lower resistance than those used in chlor-alkali cells. This may be achieved by utilizing a greater percentage graft. Preferably such membranes will have about 20% to 50% of TFS graft. This may be achieved with a higher TFS concentration or by varying the dose rates. The solvents for the grafting procedure may be aromatic compounds or halogenated compounds. Preferred solvents for the TFS and benzene and methylene chloride. Both solvents are inert and inexpensive. Methylene chloride has the further advantage of being non-flammable. The results of grafting in this solvent are shown in Table II. TABLE II______________________________________GRAFTING OFTRIFLUOROSTYRENE IN METHYLENE CHLORIDE______________________________________TFS Conc. MeCl.sub.2 Dose Rate Total Dose % Graft______________________________________10% 90% 7163 r/hr 2.49 Mrad 2.530% 70% 7163 r/hr 2.49 Mrad 9.750% 50% 7163 r/hr 2.49 Mrad 17.670% 30% 7163 r/hr 2.49 Mrad 27.1______________________________________ A comparison of the results shown in Tables I and II indicates that the use of methylene chloride as a solvent leads to a greater degree of grafting than the use of benzene. Additives may be employed to increase the rate of grafting, such as the use of a minor amount of methanol with benzene. As shown in Tables III and IV, the grafting of TFS onto the base film in dose and temperature dependent. TABLE III______________________________________ GRAFTING OF TRIFLUOROSTYRENE TO FEPFILM AT ROOM TEMPERATURE AND 60%TRIFLUOROSTYRENE IN BENZENE SOLUTION______________________________________Dose Rate Radiation Time Total Dose % Graft______________________________________12,606 r/hr 51.5 hrs. 0.649 Mrad 3.3%12,606 r/hr 121.8 hrs. 1.535 Mrad 7.2%12,606 r/hr 233.0 hrs. 2.937 Mrad 15.5%12,606 r/hr 344 hrs. 4.33 Mrad 26.1%12,606 r/hr 402 hrs. 5.06 Mrad 29.9%______________________________________ TABLE IV__________________________________________________________________________GRAFTING OF TRIFLUOROSTYRENE AT DIFFERENT TEMPERATURES__________________________________________________________________________Temperature TFS Conc.of Grafting In Benzene Dose Rate Total Dose % Graft__________________________________________________________________________-78° C 25% 7236 r/hr 3.11 Mrad 0.7% 23° C 25% 7236 r/hr 2.96 Mrad 8.3%__________________________________________________________________________ Generally the dose rate and temperature are not critical. It is possible to utilize dose rates in the range of about 5,000 r/hr up to about 300,000 r/hr. Preferably the dose rate is kept below about 100,000 r/hr. Too great a total dose may cause degradation of the base film. Generally a total dose within the range of about 0.1 to 10 Mrad is useful, while a range of about 0.7 to 5 Mrad is preferable. Higher dose rates also yield lower percentage grafts for the same total dose. The temperature may also be widely varied within the range of -78° C to 60° C; room temperature is preferred for convenience of operations. As noted above TFS can be grafted onto many base film materials, in addition to the FEP base film of the previous examples. Results obtained with several base films are shown in Table V. TABLE V__________________________________________________________________________GRAFTING OF TRIFLUOROSTYRENE IN OTHER BASE FILMS__________________________________________________________________________Polymeric TFS Conc.Film In Benzene Dose Rate Total Dose % Graft__________________________________________________________________________Teflon 25% 7236 r/hr 2.24 Mrad 6.8%High Density 25% 7236 r/hr 2.24 Mrad 5.7%PEPolypropylene 25% 7236 r/hr 2.24 Mrad 2.1%FEP Laminate* 25% 7236 r/hr 2.24 Mrad 6.0%__________________________________________________________________________ *2 mil FEP/2 mil glass/2 mil FEP Sulfonation of TFS resin has been carried out previously by dissolving the resin in suitable solvents prior to sulfonation, see U.S. Pat. No. 3,341,366. The present method allows sulfonation to be performed in situ on the grafted membrane with suitable sulfonating agents, such as chlorosulfonic acid and fluorosulfonic acid. The grafted membrane is first worked in a suitable solvent for TFS, such as methanol, benzene or methylene chloride, and then dried at about 50° C to 60° C for about 1/2 to 1 hour. A sulfonating bath is prepared by dissolving from 5 to 50% and preferably about 30% chlorosulfonic acid in a halogenated solvent such as carbon tetrachloride. The solvent should not be volatile at the sulfonation temperature and should not be sulfonatable. Generally the lower concentration chlorosulfonic acid baths are used when a sulfonated linear product is desired and the higher concentration baths are used when a cross-linked product is desired. A higher sulfonation temperature also promotes cross-linking. The membrane is then introduced into and allowed to dwell in the bath. The grafted film is left in the chlorosulfonic acid solution for a suitable period of time at an elevated temperature, i.e. for about 20 to 60 minutes, or longer, at about 130° to 155° C. The amount of sulfonation may be in the range of about 5 to about 25% as determined by the difference between the final weight of the sulfonated grafted film less the weight of the grafted film, divided by the weight of the grafted film. The film is then removed and boiled in water to convert the sulfonate groups to the acid form. The film is then added to an alkali metal hydroxide solution, such as 4-5% solution of potassium hydroxide to obtain the salt form. It has also been found that a final treatment in an anionic emulsifier is desirable to lower the resistance of the film. The results for various dwell times of the grafted film in the chlorosulfonic acid bath for a 17% grafted membrane are shown in Table VI. TABLE VI__________________________________________________________________________SULFONATION OF TRIFLUOROSTYRENE GRAFTED 5 MIL FEP FILM__________________________________________________________________________ Residence ElectricalTemperature Time % Weight Gain Resistance 40% KOH__________________________________________________________________________130° C 10 minutes 8.3% 0.97 ohm-in.sup.2140° C 10 minutes 8.5% 0.89 ohm-in.sup.2 20 7.1% 0.56 30 8.5% 0.54 60 7.8% 0.87 150 7.5% 1.10 300 5.6% 1.00155° C 10 minutes 8.5% 0.64 30 7.9% 0.49 60 7.8% 0.53 150 7.1% 0.80 300 6.9% 1.80__________________________________________________________________________ Instead of realizing a continuous weight gain with increasing time and temperature, it was found that generally sulfonation gradually decreases with time as shown in Table VI. The electrical resistance of the film, as measured in 40% KOH, goes through a minimum, so that the electrical resistance of the membrane (such as from 0.2 to 2 ohms per square inch) can be controlled by modification of residence time during sulfonation. This reduction in weight and change in electrical resistance may be due to the formation of sulfones. The hydroxyl ion diffusion across the membrane is another important property of the membrane, since the membrane should retard the diffusion of hydroxyl ions across the membrane to the anode. In the following tests the diffusion of hydroxyl ions is measured in a dialyser cell in which one side is filled with 2.5 M NaOH and the other side with distilled water. The concentration of OH - ion in the distilled water side is plotted against time. The flux of OH - is calculated from the slope of the plot as: ##EQU1## where J is the OH - flux in moles/in 2 -min c/t is the slope of the pH time plot V is the volume of half cell in liters A is the membrane area exposed in in 2 . J can be converted to units of gram/in 2 -hr by multiplying by a factor of 2.4 × 10 3 . The diffusion of OH - ions across various membranes is given in Table VII. The data is presented for TFS grafted membranes made in accordance with the present invention and conventionally grafted styrene membranes; the base film used was 2 mil FEP. TABLE VII______________________________________HYDROXYL ION DIFFUSION IN GRAFTED MEMBRANES______________________________________ Resistance OH-FLUXSAMPLE % Graft % Sulfonation (ohm-in.sup.2) (Mole/in.sup.2 -min)______________________________________TFS 26.0 8.0 0.500 1.6 × 10.sup..sup.-5TFS 32.9 8.8 0.446 1.8 × 10.sup..sup.-5TFS 17.4 7.5 5.30 2.1 × 10.sup..sup.-9Styrene 32.0 23.0 0.225 4.7 × 10.sup..sup.-5Styrene 20.0 14.0 1.86 5.4 × 10.sup..sup.-6Styrene 16.0 11.0 2.50 3.2 × 10.sup..sup.-6______________________________________ From a purely back diffusion point of view, the smaller the J values, the better the membrane. However, the smaller J value follows from a high electrical resistance. Therefore, a suitable balance between resistance and flux should be chosen for the membrane in accordance with the desired end-use of the membrane. The resistance to oxidation of a membrane is a very important property since it is related to the life of the cell. The screening test used to determine relative life involves ferrous ion catalyzed hydrogen peroxide degradation as described by Hodgdon (R. B. Hodgdon, J. Polymer Science, Part A-1, 171 (1968)). The membrane to be tested is added to 50 ml of a 3% hydrogen peroxide solution containing 1 ppm of ferrous ion. The mixture is kept at 70° C for 24 hours. The electrical resistance in 40% KOH is measured before, R o , and after, R f , the oxidation test. The weight loss under the conditions of these tests was also measured. The data in Table VIII is for TFS grafted membranes made in accordance with the present invention and conventionally grafted styrene membranes; the base film used was 2 mil FEP. TABLE VIII__________________________________________________________________________OXIDATION STABILITIES OF GRAFTED MEMBRANES__________________________________________________________________________ R.sub.o R.sub.fSAMPLE% GRAFT % SULFONATION (ohm-in.sup.2) (ohm-in.sup.2) % WT. LOSS__________________________________________________________________________TFS 25.6 8.8 0.23 3.9 17.4TFS 25.6 12.0 0.24 2.8 18.3TFS 32.9 8.8 0.50 1.67 9.9TFS 32.9 8.8 0.44 0.90 --TFS 32.9 8.8 0.45 1.28 --Styrene20.2 14.1 0.20 4.0 24.6Styrene20.2 14.1 0.23 4.4 --__________________________________________________________________________ As can be seen, the final resistance of the styrene-SO 3 H membranes was higher than the TFS-SO 3 H membrane. In addition, the weight loss of styrene-SO 3 H was also much larger under this very severe test. Most of the TFS-SO 3 H membranes still have a resistance below 3 ohm-in 2 and are considered to be operational but the styrene-SO 3 H membranes would require too high a voltage in operation. The electrolytic cells containing the ion exchange membranes of the present invention may be used for effecting the electrochemical decomposition of a number of ionizable compounds. Exemplary of the various solutions of ionizable compounds which may be electrolyzed and the products produced are aqueous solutions of alkali metal halides to produce alkali metal hydroxides and halogens; aqueous solutions of HCl to produce hydrogen and chlorine; aqueous solutions of ammonium sulfate to produce persulfates; aqueous solutions of borax to produce perborates; aqueous solutions of alkali metal hydroxides, when using an oxygen cathode, to produce peroxides; etc. Of these, the most preferred are aqueous solutions of alkali metal halides, particularly sodium chloride, and aqueous solutions of HCl. Typically, the solutions of these ionizable compounds are introduced into the anode compartment of the cell in which the electrolysis takes place. In a typical process, utilizing a sodium chloride brine as the feed to the anode compartment, the feed solution may contain from about 200 to 325 grams per liter sodium chloride. Preferably, the anolyte liquor has a pH in the range of about 1 to 5, with a pH within the range of about 2.5 to 4.0 being particularly preferred. This pH of the anolyte solution may be attained by the addition of hydrochloric acid to the feed brine solution, typically in amounts of about 2 to 10% by weight. In general, the cells may be operated over a wide temperature range, e.g., from room temperature up to the boiling point of the electrolyte although temperatures of from about 65° to 90° C are preferred. Similarly, a wide variation in the electrical operating conditions are also possible, with cell voltages of from about 0.5 to 4 amps per square inch being suitable. The concentration of the sodium hydroxide concentrations of from about 24 to 33% by weight being preferred. Typically, the sodium hydroxide recovered from the cathode compartment contains less than about 1% by weight of sodium chloride while chlorine is produced in the anode compartment at a current efficiency in excess of about 95%. In accordance with the foregoing procedure, six samples of TFS grafted FEP film were tested in a chlorine cell. All samples were preboiled for 15-20 minutes before the test. The cell used was a standard two compartment glass minicell operated between 85°-95° C. The anolyte was circulated with acidified brine at a pH of 2.0. The catholyte was 100 gm/liter sodium hydroxide. The resistance of each membrane was determined using an AC bridge. The initial voltage for the cell was determined at 2 ASI and 100 gm/liter caustic strength 85°-95° C. The cell was operated and the cell voltaged determined at various times, and corrected to the initial conditions of 100 gm/liter sodium hydroxide and the rate of voltage increase calculated. The results are summarized in Table IX. TABLE IX__________________________________________________________________________ SULFO- NATION RESIS- RATE of SULFONATION % SULFO- TIME TANCE INITIAL OPERATION FINAL INCREASENO. % GRAFT TEMPERATURE (° C) NATION (HRS.)* ohm/in.sup.2 VOLTAGE TIME (HRS) VOLTAGE mv/hr__________________________________________________________________________1. 17.4 155 reflux 7.1 2.5 0.8 3.42 170 4.93 9.02 17.4 140 7.5 2.5 1.1 3.45 129 5.25 12.73 17.4 155 7.0 5.0 1.8 3.75 520 5.14 0.284 17.4 140 8.9 0.5 0.6 3.37 543 5.69 0.315 21.37 140 9.0 0.5 0.342 3.00 555 4.50 1.046 46.2 140 12.0 0.5 0.220 2.89 384** 3.18 0.71__________________________________________________________________________ *in a 30% chlorosulfonic acid bath **Brittleness The "Operation Time" in the table for samples 1-5 was the lifetime during which the cell voltage was less than 4.5 volts. A cell voltage of 4.5 volts at 2 ASI does not necessarily mean the membrane had to be removed from the test. Depending on power costs, higher cell voltages might be economical. Also lower cell voltage could be obtained by decreasing the current density. The selection of 2 ASI as an operating current density was used as a method of screening. At lower current densities the voltage-time rise would be lower and correspondingly longer time would be projected for the membrane to reach a given cell voltage. The "Rate Of Increase" in cell voltage was determined from the linear portion of the variation in cell voltage which occurred after an initially higher rate of increase and prior to a sharp rise prior to termination of the test. For example, for samples 3 and 4, the respective initial rates of increase were 0.60 mv/hr and 1.70 mv/hr each after about 135 hours. FIG. 1 is a plot of the voltage characteristics as a function of operating time for sample 4. The use of the membrane of this invention in fuel cells may be illustrated as follows. Place the membrane in abutting relationship between two fuel cell electrodes in a conventional fuel cell configuration. The faces of the electrodes away from the membrane respectively form the sides of compartments for reactants and products of the fuel cell process, i.e. see U.S. Pat. No. 3,341,366. The electrodes may be made of platinum black and a binding agent, by techniques well known in the art. The electrodes are bonded to the membrane by the application of an elevated temperature and pressure, i.e. 250° F and 450 psi. Hydrogen gas is supplied at the anode and oxygen gas at the cathode and current is drawn from the cell by leads affixed to the electrodes. The membranes of this invention can also be used to prepare anionic exchange membranes. The procedures for this are analogous to those used for conventional styrene based anionic membranes as reported in the literature. This can be achieved, for example, with a TFS grafted membrane, by the standard chemical sequence of halomethylation, amination and quaternization, or by a nitration and reduction route. In addition to the radiation technique for grafting the perfluoro monomers described above, it has been found that these monomers may be polymerized by radiation either in bulk or in solution. The technique of radiation polymerization has the advantage over conventional catalyzed polymerization (with peroxides or persulfates) in producing a purer product, i.e., free of catalyst residues both physically admixed and chemically combined. Generally the conditions set forth above for grafting may be followed for polymerization and also for sulfonation. Using a Cobalt-60 source at room temperature, the following results were obtained. TABLE X__________________________________________________________________________RADIATION POLYMERIZATION OF TRIFLUOROSTYRENE__________________________________________________________________________TFS Conc. Benzene Conc. Dose Rate Total Dose Polymer Yield__________________________________________________________________________50 50% 7236 r/hr 1.98 Mrad 0.6%100 0% 7236 r/hr 1.98 Mrad 1.4%__________________________________________________________________________ This invention has been described in terms of specific embodiments set forth in detail. Alternative embodiments will be apparent to those skilled in the art in view of this disclosure, and accordingly such modifications are to be contemplated within the spirit of the invention as disclosed and claimed herein.

Description

Topics

Download Full PDF Version (Non-Commercial Use)

Patent Citations (4)

    Publication numberPublication dateAssigneeTitle
    US-3298942-AJanuary 17, 1967Ct Nat De La Rech Scient MinisProduction of graft copolymers of perhalogenated olefins
    US-3341366-ASeptember 12, 1967Gen ElectricSulfonated polymers of alpha, beta, beta-trifluorostyrene, with applications to structures and cells
    US-3839172-AOctober 01, 1974AnvarRadiation grafting of acrylic monomers onto perhalogenated olefin polymeric substrates
    US-3878072-AApril 15, 1975Hooker Chemicals Plastics CorpElectrolytic method for the manufacture of chlorates

NO-Patent Citations (0)

    Title

Cited By (135)

    Publication numberPublication dateAssigneeTitle
    US-2004033407-A1February 19, 2004Toru Koyama, Toshiyuki Kobayashi, Kenji Yamaga, Tomoichi Kamo, Kazutoshi HigashiyamaSolid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    US-2006292417-A1December 28, 2006Toru Koyama, Toshiyuki Kobayashi, Kenji Yamaga, Tomoichi Kamo, Kazutoshi HigashiyamaSolid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    US-7285612-B2October 23, 2007Samsung Sdi Co., Ltd.Partially fluorinated copolymer based on trifluorostyrene and substituted vinyl compound and ionic conductive polymer membrane formed therefrom
    US-7445864-B2November 04, 2008Basf Fuel Cell GmbhFunctionalized polyazoles, method for the production thereof, and use thereof
    US-6849688-B2February 01, 2005Sachem, Inc.Polymer grafted support polymers
    WO-0049069-A1August 24, 2000Mikael ParonenPolymer membrane and a process for the production thereof
    US-6774150-B2August 10, 2004Samsung Electronics Co., Ltd.Partially fluorinated copolymer based on trifluorostyrene and substituted vinyl compound and ionic conductive polymer membrane formed therefrom
    US-6630518-B1October 07, 2003Mikael ParonenPolymer membrane and a process for the production thereof
    US-8323810-B2December 04, 2012Basf Fuel Cell Research GmbhProton-conducting membrane and use thereof
    US-7972734-B2July 05, 2011Sumitomo Chemical Company, LimitedProcess for producing polymer electrolyte emulsion
    US-2010196790-A1August 05, 2010Fujifilm CorporationMembrane and electrode assembly and fuel cell
    US-5817718-AOctober 06, 1998Aisin Seiki Kabushiki KaishaSolid-polymer-electrolyte membrane for fuel cell and process for producing the same
    US-5198117-AMarch 30, 1993The Dow Chemical CompanyMethod and apparatus for preparing an epoxide by anionic dialysis
    US-5783608-AJuly 21, 1998Ebara Corporation, Japan Atomic Energy Research InstituteProcess for producing separation functional fibers and ion-exchange fibers produced therefrom
    WO-2008153153-A1December 18, 2008Sumitomo Chemical Company, LimitedMembrane-electrode assembly, method for producing the same and solid polymer fuel cell
    WO-2008153152-A1December 18, 2008Sumitomo Chemical Company, LimitedMembrane-electrode assembly, and membrane-electrode-(gas diffusion layer) assembly and solid polymer fuel cell each comprising the same
    US-5264093-ANovember 23, 1993E. I. Du Pont De Nemours And CompanyIrradiation of cation exchange membranes to increse current efficiency and reduce power consumption
    US-6964823-B2November 15, 2005Hitachi, Ltd.Solid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    WO-03096465-A1November 20, 2003Pemeas GmbhMembrane electrolyte polymere, procede de production de cette membrane et son utilisation dans des piles a combustible
    US-5876571-AMarch 02, 1999E. I. Du Pont De Nemours And CompanyProcess for making cation exchange membranes with enhanced electrochemical properties
    US-5498639-AMarch 12, 1996Ballard Power Systems Inc.Trifluorostyrene and substituted trifluorostyrene copolymeric ion-exchange membranes
    US-6437011-B2August 20, 2002Ballard Power Systems Inc.α,β, β-trifluorostyrene-based composite membranes
    US-7931995-B2April 26, 2011Gore Enterprise Holdings, Inc.Solid electrolyte composite for electrochemical reaction apparatus
    WO-2008153148-A1December 18, 2008Sumitomo Chemical Company, LimitedEncre catalytique, procédé pour fabriquer une encre catalytique, procédé pour fabriquer un ensemble membrane-électrode, ensemble membrane-électrode fabriqué par le procédé et pile à combustible
    DE-112008000381-T5December 17, 2009Sumitomo Chemical Company, Ltd.Ionenleitfähige Zusammensetzung, ionenleitfähige Folie, die diese enthält, Elektrodenkatalysator-Material und eine Brennstoffzelle
    US-4420612-ADecember 13, 1983Director Genereal Of Agency Of Industrial Science & TechnologyCatalyst membrane
    US-7745030-B2June 29, 2010Basf Fuel Cell GmbhProton-conducting polymer membrane comprising sulfonic acid-containing polyazoles, and use thereof in fuel cells
    US-6387964-B1May 14, 2002International Power PlcWater based grafting
    US-4605685-AAugust 12, 1986Chlorine Engineers Corp., Ltd.Method for preparation of graft polymeric membranes
    US-6225368-B1May 01, 2001National Power PlcWater based grafting
    US-2006210881-A1September 21, 2006Gordon Calundann, Oemer Uensal, Brian Benicewicz, Eugene ScanlonProton-conducting membrane and use thereof
    WO-9725369-A1July 17, 1997Ballard Power Systems Inc.α,β,β-TRIFLUOROSTYRENE-BASED AND SUBSTITUTED α,β,β-TRIFLUOROSTYRENE-BASED COMPOSITE MEMBRANES
    WO-2008004643-A1January 10, 2008Sumitomo Chemical Company, LimitedMethod for producing polymer electrolyte emulsion
    US-6893764-B2May 17, 2005Hitachi, Ltd.Solid polyelectrolyte, assembly of membrane and electrodes, and fuel cell
    US-7541107-B2June 02, 2009Hitachi, Ltd.Solid polyelectrolyte, assembly of membrane and electrodes, amd fuel cell
    US-5330626-AJuly 19, 1994E. I. Du Pont De Nemours And CompanyIrradiation of polymeric ion exchange membranes to increase water absorption
    US-2003096149-A1May 22, 2003Tohru Koyama, Toshiyuki Kobayashi, Kenji Yamaga, Tomoichi Kamo, Kazutoshi HigashiyamaSolid polyelectrolyte, assembly of membrane and electrodes, and fuel cell
    US-7846982-B2December 07, 2010Pemeas GmbhProton conducting electrolyte membrane having reduced methanol permeability and the use thereof in fuel cells
    WO-2011059115-A1May 19, 2011住友化学株式会社Ensemble électrode à membrane, et pile à combustible l'utilisant
    US-2005175879-A1August 11, 2005Joachim Kiefer, Oemer UensalGrafted polymer electrolyte membrane, method for the production thereof, and application thereof in fuel cells
    US-5128014-AJuly 07, 1992E. I. Du Pont De Nemours And CompanyIrradiation of cation exchange membranes
    US-2005049319-A1March 03, 2005Ballard Power Systems Inc.Graft polymeric membranes and ion-exchange membranes formed therefrom
    US-6359019-B1March 19, 2002Ballard Power Systems Inc.Graft polymeric membranes and ion-exchange membranes formed therefrom
    US-2006014065-A1January 19, 2006Pemeas GmbhMembrane electrode unit comprising a polyimide layer
    US-7625652-B2December 01, 2009Basf Fuel Cell GmbhMultilayer electrolyte membrane
    US-5622681-AApril 22, 1997The Dow Chemical CompanyDialysis separation of heat stable organic amine salts in an acid gas absorption process
    US-7638220-B2December 29, 2009Sumitomo Chemical Company, LimitedPolymeric laminates, processes for producing the same, and use thereof
    US-5773480-AJune 30, 1998Ballard Power Systems Inc.Trifluorostyrene and substituted trifluorostyrene copolymeric compositions and ion-exchange membranes formed therefrom
    US-RE37307-EAugust 07, 2001W. L. Gore & Associates, Inc.Ultra-thin integral composite membrane
    US-2005084727-A1April 21, 2005Joachim Kiefer, Oemer UensalProton conducting electrolyte membrane for use in high temperatures and the use thereof in fuel cells
    EP-1947725-A2July 23, 2008Sumitomo Chemical Company, LimitedPolymerelektrolytzusammensetzung und Brennstoffzelle
    US-4537668-AAugust 27, 1985Commissariat A L'energie AtomiqueProcess for the production of a cation exchange diaphragm and the diaphragm obtained by this process
    US-2004045814-A1March 11, 2004Bamdad Bahar, Greg Rusch, Jeffrey Kolde, Hiroshi KatoSolid electrolyte composite for electrochemical reaction apparatus
    CN-101978538-BSeptember 18, 2013昭和电工株式会社燃料电池用催化剂的制造方法和燃料电池用催化剂
    WO-2009034684-A1March 19, 2009Fujifilm CorporationAssemblage électrode-membrane et pile à combustible
    US-5994426-ANovember 30, 1999Aisin Seiki Kabushiki KaishaSolid-polymer-electrolyte membrane for fuel cell and process for producing the same
    WO-2009119903-A1October 01, 2009住友化学株式会社Composition d’électrolyte polymère
    US-6054230-AApril 25, 2000Japan Gore-Tex, Inc.Ion exchange and electrode assembly for an electrochemical cell
    US-9559367-B2January 31, 2017Basf Fuel Cell GmbhLong-life membrane electrode assemblies and its use in fuel cells
    US-6455447-B1September 24, 2002Kimberly-Clark CorporationPaper machine substrates resistant to contamination by adhesive materials
    WO-9508581-A1March 30, 1995Ballard Power Systems Inc.Compositions copolymeres a base de trifluorostyrene et de trifluorostyrene substitue, et membranes echangeuses d'ions fabriquees a partir de ces compositions
    US-2005165167-A1July 28, 2005Mackinnon Sean M.Process for preparing graft copolymers and membranes formed therefrom
    WO-9639379-A1December 12, 1996Ballard Power Systems Inc.Compositions de trifluorostyrene substituees
    US-2005244695-A1November 03, 2005Joachim Kiefer, Oemer Uensal, Gordon CalundannProton-conducting polymer membrane comprising a polymer with sulphonic acid groups and use thereof in fuel cells
    WO-2008041622-A1April 10, 2008Fujifilm CorporationEnsemble membrane électrode et procédé de production de celui-ci
    US-2006183012-A1August 17, 2006Oemer Uensal, Joachim Kiefer, Gordon Calundann, Michael Sansone, Brian Benicewiez, Choe Eui WProton-conducting polymer membrane comprising sulfonic acid-containing polyazoles, and use thereof in fuel cells
    US-7560185-B2July 14, 2009Hitachi, LtdSolid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    US-2005118477-A1June 02, 2005Joachim Kiefer, Oemer Uensal, Gordon Calundann, James CrivelloProton conducting electrolyte membrane having reduced methanol permeability and the use thereof in fuel cells
    US-2005147859-A1July 07, 2005Joachim Kiefer, Oemer Uensal, Gunter ChristMixture comprising phosphonic acid containing vinyl, polymer electrolyte membranes comprising polyvinylphoshphonic acid and the use thereof in fuel cells
    US-5602185-AFebruary 11, 1997Ballard Power Systems Inc.Substituted trifluorostyrene compositions
    CN-101691423-BJune 08, 2011中山大学, 江苏卓熙氟化科技有限公司一种氟化改性磺化聚芳醚及其制备方法和应用
    US-6080820-AJune 27, 2000E. I. Du Pont De Nemours And Company(Fluorovinyl ether)-grafted high-surface-area polyolefins and preparation thereof
    US-2004067402-A1April 08, 2004Barndad Bahar, Hobson Alex R., Kolde Jeffrey A., Mallouk Robert S.Ultra-thin integral composite membrane
    US-6613203-B1September 02, 2003Gore Enterprise HoldingsIon conducting membrane having high hardness and dimensional stability
    US-2006234099-A1October 19, 2006Klaus MuellenFunctionalized polyazoles, method for the production thereof, and use thereof
    US-2006100294-A1May 11, 2006Samsung Sdi Co., Ltd.Partially fluorinated copolymer based on trifluorostyrene and substituted vinyl compound and ionic conductive polymer membrane formed therefrom
    US-6723758-B2April 20, 2004Ballard Power Systems Inc.Graft polymeric membranes and ion-exchange membranes formed therefrom
    US-2008070274-A1March 20, 2008William Lee, Kyoichi SaitoHigh capacity, methods for separation, purification, concentration, immobilization and synthesis of compounds and applications based thereupon
    US-2006105216-A1May 18, 2006Japan Atomic Energy Agency, Nitto Denko CorporationPolymer electrolyte membrane having improved oxidation resistance
    US-2011033777-A1February 10, 2011Basf Fuel Cell Research GmbhProton-conducting membrane and use thereof
    US-2004016693-A1January 29, 2004Ballard Power Systems Inc.Process for preparing graft copolymer membranes
    US-2005256296-A1November 17, 2005Joachim Kiefer, Gordon Calundann, Oemer Uensal, Jochen Baurmeister, Frauke JordtPolymer film based on polyazoles, and uses thereof
    US-2006166067-A1July 27, 2006Joachim Kiefer, Oemer UensalPolymer electrolyte membrane, method for the production thereof, and application thereof in fuel cells
    US-6350925-B1February 26, 20023M Innovative Properties CompanyPerhaloethyl aromatic compounds and perhaloethenyl aromatic compounds therefrom
    US-5422411-AJune 06, 1995Ballard Power Systems Inc.Trifluorostyrene and substituted trifluorostyrene copolymeric compositions and ion-exchange membranes formed therefrom
    US-5798417-AAugust 25, 1998E. I. Du Pont De Nemours And Company(Fluorovinyl ether)-grafted high-surface-area polyolefins and preparation thereof
    US-2005181254-A1August 18, 2005Oemer Uensal, Joachim KieferMultilayer electrolyte membrane
    US-7332530-B2February 19, 2008Celanese Ventures GmbhProton-conducting polymer membrane comprising a polymer with sulphonic acid groups and use thereof in fuel cells
    US-5684192-ANovember 04, 1997Ballard Power Systems, Inc.Substituted trifluorostyrene monomeric compositions
    US-4200538-AApril 29, 1980Toyo Soda Manufacturing Co. Ltd.Process for preparing cation-exchange membrane
    US-6638579-B2October 28, 2003Kimberly-Clark Worldwide, Inc.Process of making paper machine substrates resistant to contamination by adhesive materials
    US-6242123-B1June 05, 2001Aisin Seiki Kabushiki KaishaSolid polyelectrolyte membrane for fuel cells, and method for producing it
    WO-2008153145-A1December 18, 2008Sumitomo Chemical Company, LimitedEnsemble film-électrode, ensemble film-électrode-couche de diffusion de gaz comprenant cet ensemble, pile à combustible à polymère semi-conducteur et procédé de fabrication de l'ensemble film-électrode
    US-2007292734-A1December 20, 2007Joachim Kiefer, Oemer UensalPolymer electrolyte membrane, method for the production thereof, and application thereof in fuel cells
    US-5548055-AAugust 20, 1996Sri InternationalSingle-ion conducting solid polymer electrolytes
    US-2010047669-A1February 25, 2010Basf Fuel Cell GmbhMultilayer electrolyte membrane
    US-5743940-AApril 28, 1998Japan Atomic Energy Research Institute, Ebara CorporationProcess for producing gas adsorbent
    US-7820314-B2October 26, 2010Basf Fuel Cell Research GmbhProton-conducting membrane and use thereof
    US-7919537-B2April 05, 2011Japan Atomic Energy Agency, Nitto Denko CorporationMethods for producing a polymer electrolyte membrane having improved oxidation resistance
    US-7037950-B2May 02, 2006Samsung Sdi Co., Ltd.Partially fluorinated copolymer based on trifluorostyrene and substituted vinyl compound and ionic conductive polymer membrane formed therefrom
    US-5998559-ADecember 07, 1999Sri InternationalSingle-ion conducting solid polymer electrolytes, and conductive compositions and batteries made therefrom
    US-2006008690-A1January 12, 2006Oemer Uensal, Joachim Kiefer, Gordon Calundann, Michael Sansone, Brian Benicewicz, Choe Eui WonProton conducting polymer membrane comprising phoshphonic acid groups containing polyazoles and the use thereof in fuel cells
    WO-2008056824-A1May 15, 2008Sumitomo Chemical Company, LimitedEnsemble électrode à membrane
    US-7736778-B2June 15, 2010Basf Fuel Cell GmbhProton conducting polymer membrane comprising phosphonic acid groups containing polyazoles and the use thereof in fuel cells
    EP-0140544-A2May 08, 1985CHLORINE ENGINEERS CORP., Ltd.Méthode de préparation de membranes polymères de greffe et membranes d'échanges d'anions et de cations
    US-2005271922-A1December 08, 2005Toru Koyama, Toshiyuki Kobayashi, Kenji Yamaga, Tomoichi Kamo, Kazutoshi HigashiyamaSolid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    US-2006166047-A1July 27, 2006Sumitomo Chemical Company, LimitedPolymeric laminates, processes for producing the same, and use thereof
    US-2005031930-A1February 10, 2005Tohru Koyama, Toshiyuki Kobayashi, Kenji Yamaga, Tomoichi Kamo, Kazutoshi HigashiyamaSolid polyelectrolyte, assembly of membrane and electrodes, amd fuel cell
    US-4132682-AJanuary 02, 1979Toyo Soda Manufacturing Co., Ltd.Process for preparing cation-exchange membrane
    US-7795372-B2September 14, 2010Basf Fuel Cell GmbhPolymer film based on polyazoles, and uses thereof
    US-7300984-B2November 27, 2007Ballard Power Systems Inc.Process for preparing graft copolymers and membranes formed therefrom
    US-6127433-AOctober 03, 2000Ebara Corporation, Japan Atomic Energy Research InstituteProcess for producing separation functional fibers and ion-exchange fibers produced therefrom
    US-6765027-B2July 20, 2004Ballard Power Systems Inc.Ion-exchange materials with improved ion conductivity
    US-7125626-B2October 24, 2006Japan Gore-Tex, Inc.Ion exchange assembly for an electrochemical cell
    WO-2008153151-A1December 18, 2008Sumitomo Chemical Company, Limited膜-電極接合体及びその製造方法、並びに固体高分子形燃料電池
    EP-2036927-A1March 18, 2009Fujifilm CorporationIonische Polymerteilchenverteilungsflüssigkeit und Herstellungsverfahren dafür
    DE-112010004052-T5December 06, 2012Sumitomo Chemical Co., Ltd.Polymerelektrolytmembran, Membran-Elektroden-Anordnung und Festkörperpolymer-Brennstoffzelle
    EP-0140544-A3December 02, 1987CHLORINE ENGINEERS CORP., Ltd.Méthode de préparation de membranes polymères de greffe et membranes d'échanges d'anions et de cations
    DE-19844645-B4November 24, 2005Aisin Seiki K.K., KariyaFestkörper-Polyelektrolytmembran für Brennstoffzellen und Verfahren zu deren Herstellung
    US-2009208804-A1August 20, 2009Ryuma Kuroda, Shin Saito, Hiroyuki Kurita, Kentaro MasuiPolymer electrolyte emulsion and use thereof
    US-2005238932-A1October 27, 2005Tooru Koyama, Osamu Kubota, Hidetoshi Honbou, Kenichi SoumaFuel cell power source, method of operating thereof and portable electronic equipment
    US-7846983-B2December 07, 2010Basf Fuel Cell GmbhProton conducting electrolyte membrane for use in high temperatures and the use thereof in fuel cells
    CN-101808739-BOctober 16, 2013昭和电工株式会社催化剂及其制造方法以及其用途
    US-2004009305-A1January 15, 2004Ballard Power Systems Inc.Process for preparing graft copolymer membranes
    EP-2037525-A1March 18, 2009FUJIFILM CorporationElectrolyte membrane, membrane and electrode assembly and fuel cell using membrane and electrode assembly
    US-2004086764-A1May 06, 2004Mikael ParonenPolymer membrane and a process for the production thereof
    US-6902849-B2June 07, 2005Mikael ParonenPolymer membrane and a process for the production thereof
    US-2009208810-A1August 20, 2009Ryuma Kuroda, Shin Saito, Hiroyuki Kurita, Kentaro MasuiProcess for producing polymer electrolyte emulsion
    US-2006079594-A1April 13, 2006Charles StoneProcess for preparing graft copolymer membranes
    US-7553574-B2June 30, 2009Hitachi, LtdSolid polymer electrolyte, a membrane using thereof, a solution for coating electrode catalyst, a membrane/electrode assembly, and a fuel cell
    US-6828386-B2December 07, 2004Ballard Power Systems Inc.Process for preparing graft copolymers and membranes formed therefrom
    WO-2008004644-A1January 10, 2008Sumitomo Chemical Company, LimitedÉmulsion d'électrolyte polymère et utilisation de celle-ci
    US-2003113604-A1June 19, 2003Bamdad Bahar, Hobson Alex R., Kolde Jeffrey A., Mallouk Robert S.Fuel cell comprising a composite membrane
    US-2003152820-A1August 14, 2003Hiroshi KatoIon exchange assembly for an electrochemical cell
    US-2010047661-A1February 25, 2010Sumitomo Chemical Company, LimitedPolymer laminate membrane, the method for producing the membrane and the use of the membrane